一、牌號和化學成分
|
牌號 |
化學成分(質量分數(shù))(％) |
|||||||
|
C |
Si |
Mn |
P |
S |
Cu |
Cr |
Ni |
|
|
09CuPCrNi—A |
≤0.12 |
0.25-0.75 |
0.20-0.50 |
0.07-0.15 |
≤0.040 |
0.25-0.55 |
0.30-0.25 |
≤0.65 |
|
09CuPCrNi—B |
≤0.12 |
0.10-0.40 |
0.20-0.50 |
0.07-0.12 |
≤0.040 |
0.25-0.45 |
0.30-0.65 |
0.25-0.50 |
|
09CuP |
≤0.12 |
0.20-0.40 |
0.20-0.50 |
0.07-0.12 |
≤0.040 |
0.25-0.45 |
|
|
二、力學和工藝性能
|
牌號 |
交貨狀態(tài) |
厚度 ／mm |
屈服點ós |
抗拉強度ób |
伸長率δ5(％)≥ |
180°冷彎試驗 |
V型缺口沖擊試驗 沖擊吸收功AK/J |
|
MPa≥ |
|||||||
|
09CupCrNi—A |
熱軋 |
≤6 >6 |
345 |
480 |
22 |
d=a d=2a |
平均≥27.5 條件：12-16mm、 厚、0℃、縱向 |
|
09CupCrNi—B |
≤6 >6 |
295 |
430 |
24 |
d=a d=2a |
||
|
09Cup |
≤6 >6 |
295 |
415 |
24 |
d=a d=2a |
||
|
09CupCrNi—A |
冷軋 |
≤2.5 |
315 |
450 |
26 |
d=a |
|
|
09CuPCrNi-B09CuP |
265 |
405 |
27 |
||||